Effect of maleic anhydride grafted triblock copolymer of poly(styrene-b-ethylene-co-butylene-b-styrene) (SEBS-g-MA) on the morphology of the blends of polyamide 6 (PA6) and maleated polypropylene (PP-g-MA) was investigated by small angle x-ray scattering, differential scanning calorimeter and scanning electron microscopy. The size of the dispered PA6 decreased with addition of SEBS-g-MA. SEBS-g-MA reacted with the amine group of PA6 during the melt-compounding, and as a result, the copolymer, formed by interfacial reaction between PA6 and SEBS-g-MA, led to reduction in size of the dispersed PA6. SEBS-g-MA was partially microphase-separated to dispersion phase, and its size increased proportional to the amount of added SEBS-g-MA and increased temperature. The microphase-separated dispersion phase highly affected the crystallinity of the PP-g-MA matrix and PA6 dispersion.

Polyamide 6 (PA6)/maleated polypropylene (PP-g-MA) 블렌드계의 상용화제로 maleic anhydride (MA)가 그래프트(graft)된 poly(styrene-b-ethylene-co-butylene-b-styrene) (SEBS-g-MA)를 첨가하여 블렌드의 고차구조에 미치는 영향을 small angle x-ray scattering, DSC 및 SEM을 이용하여 고찰하였다. SEBS-g-MA가 첨가된 시료는 첨가되지 않은 시료보다 PA6분상의 크기가 작았는데 이는 가공 또는 열처리 중 SEBS-g-MA의 무수말레산과 PA6의 아민 그룹(amine group) 사이에 반응이 일어나 PA6/PP-g-MA 계면에 PA6-SEBS-g-MA 그래프트 공중합체가 형성되어 이 공중합체가 상용화제로서 작용하여 계면장력을 안정화시켜 PA6 분산상 크기를 작게 한 것으로 추정되었다. 첨가된 SEBS-g-MA의 일부는 마이크로 상분리(Micro-phase separation)되어 미세 분산상으로 존재하게 되는데 그 크기는 첨가된 양이 많을수록, 저온보다 고온일수록 크다는 것이 관찰되었다. 미세 분산상 SEBS-g-MA는 PP-g-MA 연송상의 결정화도를 낮추는 반면, PA6 분산상의 결정화도는 증가시켰다.