Poly(3,4-ethylenedioxythiophene) : poly(styrenesulfonate) (PEDOT : PSS) has attracted a great deal of attention as a transparent conductive material for organic solar cells or organic light-emitting diodes due to its high electrical conductivity, optical transparency, and excellent mechanical flexibility. It is well known that a solvent doping for PEDOT : PSS thin-films significantly increases the conductivity of films. In this paper, the effect of various kinds of solvent doping and post-treatment on the electrical and structural properties of PEDOT : PSS thin-films is investigated. The solvent doping greatly increases the conductivity of PEDOT : PSS thin-films up to 884 S/cm. A further enhancement of the conductivity of PEDOT : PSS thin-films is achieved by the solvent post-treatment which raises the conductivity up to 1131 S/cm. The enhancement is mainly caused by the depletion of insulating PSS and forming conducting PEDOT-rich granular networks. Strong optical absorption peaks at the wavelength of 225 nm of PEDOT : PSS thin-films indicate the depletion of insulating PSS by post-treatment. We believe that the solvent post-treatment is a promising method to achieve highly conductive transparent PEDOT : PSS thin-films for applications in efficient, low-cost and flexible organic devices.

전도성 고분자인 poly(3,4-ethylenedioxythiophene) : poly(styrenesulfonate) (PEDOT : PSS)는 우수한 전기 전도도와 광투과 도, 유연성을 가지고 있기 때문에 유기태양전지와 유기발광소자의 투명전극으로서 많은 각광을 받고 있다. PEDOT : PSS 의 전기 전도도는 솔벤트를 도핑함에 따라 큰 폭으로 증가한다는 사실은 잘 알려져 있다. 본 연구에서는 다양한 솔벤트 의 도핑과 솔벤트 후처리 공정에 따른 PEDOT : PSS 박막의 전기 전도도와 구조적 특성 변화를 연구하였다. 솔벤트 도핑으로 PEDOT : PSS의 전도도는 884 S/cm까지 증가하였고, 후처리 공정을 통해서 1131 S/cm의 전도도 값을 얻을 수 있었다. 이러한 전도도의 증가는 PSS 물질이 빠져나가거나 구조적인 재배열에 따른 전도성 PEDOT 입자의 접촉 면적이 증가함에 따른 것으로 사료되고, 광학적인 방법으로 PSS의 추출을 관찰하였다. 솔벤트 후처리 공정은 PEDOT : PSS 박막의 전도도를 향상하는 매우 효과적인 방법으로 확인되었고, 저가형 플렉서블 유기전자소자의 투명전극으로써의 사용이 적합할 것으로 예상된다.