Original article : Preparation and Properties of Silicone-Modified Epoxy Coating Materials

Jin Kyung Kim

Abstract

PDMS modified epoxy resin with epoxy group (EMPDMS) was prepared from the reaction of α,ω-aminopropylpolydimethylsiloxaneand diglycidyl ether of bisphenol-A (DGEBA) based epoxy resin, and PDMS modified epoxy hybrid compound (EMPDMSH)was prepared by introducing alkylesteraminopropyl alkoxy silane to EMPDMS. Their structures were characterized usingFT-IR, 1H-NMR and 29Si-NMR. Coating materials were prepared by mixing EMPDMSH base and solvent. Physical propertiesof the coating materials coated on epoxy/glass fiber composite film were measured according to the content of PDMS inEMPDMSH. Contact angle of coating film was increased 30 to 71 degree. Adhesive property of coating film was 5B degreebetter then epoxy or acrylate coating materials, and surface roughness was decreased as increasing in EMPDMSH.

실리콘 변성 에폭시 코팅 액의 제조와 물성

김진경,박승우

초록

α,ω-Aminopropylpolydimethylsiloxane을 bisphenol-A diglycidyl ether (DGEBA)계 이관능성 에폭시 수지와 반응시켜 polydimethylsiloxane(PDMS)의 양 말단에 에폭시가 도입된 실리콘 변성 에폭시 수지(EMPDMS)를 제조한 다음 alkylesteraminopropylalkoxy silane (XD 5607)을 반응시켜 PDMS가 도입된 에폭시 hybrid 화합물(EMPDMSH)을 제조하고 이를FT-IR, 1H-NMR 및 29Si-NMR로 구조를 확인하였다. EMPDMSH base 수지에 용매를 혼합하여 코팅 액을 제조하였으며,이를 에폭시/유리 섬유 복합재료로 얻어진 필름에 도포하고 경화시킨 후 base수지 중에 함유된 PDMS의 함량에 따른물성을 측정하였다. 코팅 면의 접촉각을 측정한 결과 기존의 에폭시 수지로 코팅하여 얻은 코팅 면에 비해 접촉각이41 ° 에서 71 °로 약 30 ° 정도 증가되고 있어 코팅 면에 PDMS가 나타나 있음을 확인할 수 있었다. 또한 접착력 및표면 평활도 개선효과 측정 결과 에폭시 자체 코팅 액이나 일반적으로 많이 사용되고 있는 아크릴계 코팅 액 보다5B 등급의 뛰어난 접착력을 나타내었고 평활도 개선 효과도 우수함을 나타내었다.