In this work, the combustive properties of the swine manure, poultry manure, and mixtures based on the resource recycling-energy were investigated. After the specimens were dried to a constant weight by dry oven, combustive properties were tested by the cone calorimeter (ISO 5660-1). It was found that the peak effective heat of combustion (PEHC) in the swine manure (78.72 MJ/kg) has risen due to more amount of the hydrocabon compared with poultry manure (69.41 MJ/kg), also the swine manure increased both of the higher CO2 production rate (0.1959 g/s) and total smoke release rate (THRR) (419 m2/m2) than those of the poultry manure. However, both of the CO production release (0.0996 kg/kg) and CO production rate (0034 g/s) in the poultry manure increased due to more amount of the inorganic contents compared with swine manure. Thus, the high combustion energy is expected to generate depend on the hydrocarbon content.

본 연구에서는 자원 재활용-에너지에 바탕을 둔 돈분, 계분, 혼합물의 연소특성에 대하여 고찰하였다. 시험편은 건조 오븐을 이용하여 항량까지 건조시킨 후에, 콘칼로리미터(ISO 5660-1)를 이용하여 연소성질을 시험하였다. 그 결과 돈분의 최대유효연소열(78.72 MJ/kg)은 계분(69.41 MJ/kg)과 비교하여 탄화수소의 많은 양 때문에 비교적 증가했다. 또한 돈분의 CO2 발생속도(0.1959 g/s)와 총연기발생률(419 m2/m2)도 각각에 대하여 계분보다 증가하였다. 반면에 계분의 CO 발생량(0.0996 kg/kg)과 CO 발생속도(0.0034 g/s)는 계분이 함유하고 있는 많은 무기물 함량 때문에 각각 돈분보다 높았다. 따라서 높은 연소 에너지는 탄화수소 함량에 의존하여 발생되는 것으로 판단된다.