Original article : UV Curing and Peeling Characteristics of Acrylic Coating Ink with Various Amounts of Photoinitiator, Oligomer and Talc

Jee Woo Yang

Abstract

As the usuage of tempered glass for touch panel increased rapidly with the development of industry, the amount of UV curable coating solution used to protect glass surfaces during a tempered glass manufacturing process increased as well. The UV curable coating has advantages compared to thermal curing such as shortened curing time and non-solvent. Appropriated polymer and monomer were used as an acid polymer to grant an alkali peeling ability. The monomers were 2-hydroxyl methylacrylate, 1,6-hexanediol diacrylate and dipentaerythritol hexaacrylate which have acryl groups of 1, 2, and 6, respectively. The combination of three different types of photoinhibitors were used and bisphenol A epoxy diacrylate was used as an oligomer. In this study, experiments were carried out by controlling the amount of photoinitiator, oligomer, and additive while maintaining the constant content of the acid polymer and the acrylic monomer. The changes in physical properties according to the additive content were investigated. It was found that the combination of photoinitiators was necessary to achieve the hardness above 4H and it was possible to control the delamination type of the coating film from a sheet to pieces by the addition of TPO as an initiator. The increase in oligomer contents increased the hardness and adhesiveness alongside dissection time. Talc content of 20 wt% showed the best results.

광개시제, 올리고머 그리고 Talc 함량에 따른 아크릴계 코팅제의 UV경화 및 박리특성

양지우,서아영

초록

전자·통신 산업의 발달로 터치 패널용 강화유리의 사용량이 급격히 증가함에 따라, 판유리 가공 공정 중 유리표면을 보호하기 위한 용도로 사용되는 UV경화형 코팅용액의 사용량이 함께 증가하고 있다. UV경화형 코팅은 열경화형에 비해 경화시간이 매우 짧고, 용제를 사용하지 않는 장점이 있다. 알칼리에 의한 박리 특성을 부여하기 위해 산성 고분자styrene-acrylic acid copolymer를, 모노머로는 아크릴기가 각각 1개, 2개, 6개인 2-hydroxyl methylacrylate, 1,6-hexanediol diacrylate 그리고 dipentaerythritol hexaacrylate를 사용하였다. 광개시제로는 HP-8, TPO 및 DETX 3종을 조합하여 사용하였고 올리고머로는 bisphenol A epoxy diacrylate를 사용하였다. 본 연구에서는 산성 고분자와 아크릴계 모노머의 함량을 일정하게 유지하면서 광개시제, 올리고머, 그리고 첨가제인 talc의 함량을 변화시키며 실험을 수행하여 광개시제에 따른 제반 물성의 연계성을 고찰하였다. 시험결과 두 가지 이상의 광개시제를 사용해야 경도를 4H 이상 얻을 수 있었고 특히 TPO를 첨가하면 코팅막의 박리 형태를 시트형태로부터 조각형태로 조절하는 것이 가능하였다. 올리고머 함량이 증가하면 경도와 접착성이 증가하지만 박리시간 역시 증가하였고 talc 함량은 20 wt%에서 가장 우수한 결과를 나타내었다.