Conjugated linoleic acid methylester was synthesized through isomerization of linoleic acid methylester by using heteroge-neous catalysts. As for heterogeneous catalysts, Ni supported zeolite type catalysts were used. H zoelite Y (HY) were ion exchanged with KCI aqueous solution to synthesize K zeolite Y (KY), and with impregnation method, Ni supported zeolite catalysts were synthesized. Catalysts were used after pre-treatment by using hydrogen. HY catalysts showed a high conversion at low temperatures; but a low selectivity for conjugation reaction. KY catalysts showed a low conversion at low temperatures; but a similar conversion with HY catalysts at high temperatures while a high selectivity at low temperatures. As a result, 4 wt% Ni/KY720 recorded the high conjugation yield of 63.4% at 220.

공액 리놀레산 메틸에스테르는 불균일계 촉매인 니켈 담지 제올라이트계 촉매를 이용하여 리놀레산 메틸에스테르의 이성질화를 통해 합성할 수 있다. 니켈 담지 제올라이트계 촉매는 HY 제올라이트로부터 KCI 수용액을 이용해 이온교환 하여 KY 제올라이트를 합성한 뒤 함침법을 통해 니켈을 담지하여 합성하였다. 합성된 촉매는 수소를 이용하여 전처리 하여 공액화 반응에 사용하였다. 그 결과 낮은 온도에서 HY 촉매는 높은 전환율을 나타내었지만 공액화 반응에 대해 낮은 선택도를 나타내었다. KY 촉매는 낮은 온도에서 상대적으로 낮은 전환율을 나타내었으나 높은 온도에서 HY 촉매와 유사한 전환율을 보였으며, 낮은 온도에서도 공액화 반응에 대해 높은 선택도를 나타내었다. 결과적으로 반응 온도 220 ℃에서 4 wt% Ni/KY720을 이용하여 가장 높은 63.4%의 수율을 얻었다.