In this study, the TiO2 nano spheres were synthesized by Sol-gel method to give an excellent UV-blocking effect and increase waste adsorption. The pH value was adjusted to obtain a superb UV-blocking effect and adsorption capacity due to the high surface area which is the characteristics of porosity. Base treated TiO2 showed outstanding characteristics. The adsorption of gycerine onto the TiO2 sample using TGA resulted in a high surface area of 1.16 mg/mg. This also showed a high reflectance in the UV-A region. In order to find the optimum dispersion, inorganic powder particles were maintained their sizes as 180 nm for about 6 months. The size of particles were measured using ester oil and silicon oil. Overall, the results reveal that TiO2 has an excellent capability sunscreen in the UV-A region and skin waste adsorption.

본 연구에서 제조한 나노구형체 TiO2는 자외선 차단 효과가 우수하면서도 노폐물 흡착을 하는 기능을 부여하기 위해 Sol-gel 방법으로 합성하였다. 다공성의 특성으로 높은 표면적에 의한 우수한 자외선 차단효과 및 흡착능력을 얻기 위해 pH를 조절하였다. 염기 처리한 TiO2의 경우 가장 우수한 특성을 나타내었다. TGA로 글리세린을 흡착한 결과 1.16 mg의 높은 흡착 결과를 얻을 수 있었다. 또한 UV-A 영역에서 높은 반사율을 가지는 것을 확인하였다. 무기분체 의 최적의 분산제를 찾기 위해 ester oil과 silicon oil를 사용하여 입도크기를 측정하였으며 180 nm정도의 입자로 약 6개월간 유지되었다. 이 결과를 통해, UV-A영역에서 우수한 능력을 가진 자외선 차단제로서 노폐물 흡착능력을 가진 TiO2를 제조했으며 이로 인한 다양한 응용이 가능할 것으로 기대된다.