Poymer blends of two degradable aliphatic polyesters, relatively expensive material polylactic acid (PLA) and relatively inexpensive material poly(butylene adipate-co-terephthalate) (PBAT), were used in this study. Three different kinds of modifiers were used with various amounts. Diisocyanate type methylenediphenyl 4,4`-diisocyanate (MDI) and hexamethylene diisocyanate (HDI) were used as modifiers and epoxy type coupling agents also used. The melt flow index (MFI) and dynamic viscoelasticity of various compositions of PLA/PBAT blends were studied. The mechanical property and morphology with respect to the fracture surface of PLA/PBAT blends were also investigated using tensile test and field emission scanning electronic microscopy, respectively. These tests were also used to verify the compatibility of PLA/PBAT and the effect of mechanical properties due to the use of modifiers. Tensile properties of PLA/PBAT blends modified with HDI were improved remarkably.

본 연구에서는 생분해성 지방족 폴리에스터 중 비교적 고가인 poly(butylene adipate-co-terephthalate) (PBAT)와 상대적 으로 저가의 생분해성 고분자인 polylactic acid (PLA)의 블렌드에 3종류의 개질제를 사용하여 그 효과를 조사하였다. 개질제로는 에폭시계의 커플링제와 diisocyanate계열의 methylenediphenyl 4,4`-diisocyanate (MDI)와 hexamethylene diisocyanate (HDI)를 사용하였다. 여러 가지 조성의 블렌드에 용융흐름지수, 동적 점탄성을 조사하였다. 또한, 인장 시험을 통한 기계적 물성 조사와 FE-SEM으로 시편의 파단표면을 관찰하였다. 이를 통해 PLA/PBAT 블렌드의 상용성과 개질제의 효과 및 기계적물성에 미치는 영향을 고찰하였다. 개질제로 HDI를 사용했을 때 PLA/PBAT의 인장물성이 크게 증가하였다.