Possibility of the selective removal of Ca 2+ ions from a mixed solution of Na + and Ca 2+ ions using membrane capacitive deionization (MCDI) was investigated. Adsorption equilibrium experiments were conducted to determine the selectivity of the CMX cation-exchange membrane toward Ca 2+ ions. In addition, desalination experiments for a mixed solution (5meq/L NaCl + 2meq/L CaCl2) were performed using an MCDI cell. The adsorption equilibrium of CMX membrane showed that the equivalent fraction of Ca 2+ ions in the solution and the CMX membrane were 28.6 and 87.2%, respectively, which indicates the CMX membrane`s high selectivity toward Ca 2+ ions. Desalination experiments were performed by applying a constant current to the MCDI cell until the cell potential reached 1.0 V. The amount of ions adsorbed did not significantly change as the applied current was changed. However, the equivalent fractions of Ca 2+ ions among the adsorbed ions were inversely proportional to the applied currents: 81.4, 78.4, 77.0, and 74.5% at 200, 300, 500, and 700 A/m 2 of applied current density, respectively. This result is attributed to the increased fraction of Ca 2+ ions adsorbed by the CMX membrane at lower applied current densities.

막결합 축전식 탈염(MCDI) 기술을 이용하여 Na +와 Ca 2+ 이온이 혼합된 용액에서 Ca 2+ 이온의 선택적 제거 가능성을 연구하였다. 양이온교환막인 CMX막에 대한 Ca 2+ 이온의 선택성을 확인하기 위해 흡착평형 실험을 실시하였다. 그리 고 MCDI 셀을 이용해 혼합용액(5 meq/L NaCl + 2 meq/L CaCl2)에 대한 탈염실험을 수행하였다. 흡착평형 실험결과 용액과 CMX막에서 Ca 2+ 이온의 당량분율은 각각 28.6, 87.2%를 보여 CMX막이 Ca 2+ 이온에 대해 높은 선택성을 갖는 것을 확인하였다. MCDI 셀에 일정한 전류를 인가하면서 셀 전위가 1.0 V에 도달할 때까지 탈염실험을 실시하였다. 그 결과 흡착된 이온의 총량은 인가한 전류밀도에 큰 영향을 받지 않고 일정하였다. 그러나 흡착된 이온 중 Ca 2+ 이온의 비율은 전류밀도에 반비례하였으며 200, 300, 500, 700 A/m 2의 전류밀도에서 각각 81.4, 78.4, 77.0, 74.5%로 나타났다. 이러한 결과는 낮은 전류밀도에서 CMX막에 흡착된 Ca 2+ 이온의 비율이 높았기 때문인 것으로 판단된다.