Poly (olefin ketone) terpolymer having excellent mechanical properties was synthesized and composite materials of poly (olefin ketone) containing polyurethane/amino silane functionalized glass fibers were prepared. The compatibilities between the functionalized glass fiber and the polymer were characterized by observing the fracture surfaces of the composites using scanning electron microscopy (SEM). Mechanical properties of composites with different contents, diameters, lengths, and binders of glass fibers were also studied using universal testing machine (UTM). The introduction of suitably functionalized glass fiber into the poly (olefin ketone) produces composite materials having excellent mechanical properties and they are very promising alternative materials for the engineering plastic applications.

우수한 기계적 강도를 가지고 있는 폴리올레핀케톤 고분자를 합성하고, 우레탄과 아미노실란으로 표면 처리 된 유리 섬유를 도입하여 엔지니어링 플라스틱용 복합재료를 제조하였다. 유리섬유와 폴리올레핀케톤의 상용성을 확인하기 위해 주사 전자 현미경으로 복합재료의 파단면 형상을 확인하였고, 함유된 유리섬유의 크기와 양, 그리고 바인더의 종류에 따른 복합재료의 기계적 물성을 관찰하였다. 적절한 표면처리를 한 유리섬유로 강화된 폴리올레핀케톤 복합재 료는 좋은 계면 상용성을 보이며 향상된 기계적 강도를 가지고 엔지니어링 플라스틱 분야에서의 응용 가능성을 확인 할 수 있었다.