Nanocomposites were fabricated as titanium dioxide (TiO2) doped with nanometals (Au, Ag) by sonochemical reduction method and sol-gel method in order to investigate their antimicrobial activities. Then, the antimicrobial activity of the resulting samples was compared by the measurement of colony numbers survived on the agar plate incubated for 24 h after the loading E. coli on the solid-state media with the nanocomposites. The initial antimicrobial activity of the metal (Au, Ag)-doped TiO2 was higher than that of the pristine TiO2. Afterwards the nanocomposite samples were kept at 4 ℃ for a long time and the aged samples exhibited the different antimicrobial activity. With the elapse of aging times, Ag-doped TiO2 with TiO2 coating (Ag-TiO2@TiOx) exhibited the higher antimicrobial activity than those of Ag-TiO2 and Au-TiO2. The TiO2 coating on the Ag-TiO2 may prevent the oxidation of Ag nanometals and stabilize colloidal nanocomposites.

항균 활성도를 조사하기 위해 이산화티탄미립자 표면에 나노메탈(Au, Ag)을 균일하게 도핑한 나노복합체(Ag-TiO2, Au-TiO2, Ag-TiO2@TiOx)를 초음파환원법과 졸-겔 법으로 제조하였다. 이렇게 제조된 나노메탈-이산화티탄 복합체의 항균 활성도는 고체배지 표면에 나노복합체와 함께 E. coli를 도말하여 37 ℃에서 배양한 후 생존된 콜로니 개수의 측정을 통해서 이루어졌다. 나노복합체의 초기 항균 효율은 나노메탈이 도핑된 이산화 티탄미립자(Ag-TiO2, Au-TiO2, Ag-TiO2@TiOx) 복합체가 도핑 하지 않은 이산화 티탄미립자(TiO2)에 비해 높은 항균 효율을 나타내주었다. 이후, 나노 복합체를 4 ℃에서 보관 후 장기보관에 따른 항균특성을 비교해본 결과, 나노메탈만 도핑된 복합체(Ag-TiO2, Au-TiO2) 보다는 Ag-TiO2의 표면을 다시 산화티탄막으로 코팅한 복합체(Ag-TiO2@TiOx)의 항균특성이 오랫동안 유지되는 것을 알 수 있었다. 이는 산화티탄막으로 다시 코팅한 Ag-TiO2@TiOx의 경우에 Ag 나노 메탈의 산화방지 및 나노 복합체의 콜로이드 안정성 향상이 이루어졌기 때문으로 사료된다.