In this work, we have prepared the nanocomposite by the reaction of mica and zinc oxide, and investigated the application of nanocomposite to UV protecting creams. Mica treated with 3-aminopropyltrimethoxysilane (APTMS) reacted with 1,4-phenylenediisothiocyanate (PDC) to give -N=C=S functionalized surface, which was further reacted with zinc oxides coated with APTMS to give mica-zinc oxide nanocomposites. The composites were characterized by EA, EDS, TGA, SEM, zeta potential measurement, powder XRD, and DRS UV/Vis analyses. Finally, we measured transmittances of ultraviolet protection creams manufactured by using mica composite covered with zinc oxides in the range of 280∼400 nm. The nanocomposites developed in this work might be applicable as inorganic hybrid materials for UV protecting creams.

본 연구에서는 마이카와 산화 아연을 이용하여 복합 재료를 제조하고, 이를 자외선 차단 크림에 응용하는 연구를 수행 하였다. 먼저 마이카와 산화 아연을 각각 3-aminopropyltrimethoxysilane (APTMS)으로 처리하여 표면에 아민기를 생성 시켰다. 아민기가 붙은 마이카를 1,4-phenylenediisothiocyanate (PDC)와 반응시켜 표면에 -N=C=S 작용기를 활성화시킨 후, 아민기가 붙어있는 산화 아연과 결합시켜 산화 아연으로 덮인 마이카 복합 재료를 합성하였다. 원소 분석, EDS 분석, 열 중량 분석, SEM 이미지 분석, 형광 이미지 분석, 제타 전위 측정, X-선 회절 분석, DRS UV/Vis 분석을 통하여 고체 생성물의 특성을 규명하였다. 최종적으로 표준 프로토콜로 제조된 자외선 차단 크림의 파장에 따른 투과도를 280∼400 nm 범위에서 측정하여 자외선 차단 효과를 확인하였다.