In this work, carbon fibers were electrolessly Ni-plated in order to investigate the effect of metal plating on the electromagnetic shielding effectiveness (EMI-SE) of Ni-coated carbon fibers-reinforced epoxy matrix composites. The surfaces of carbon fibers were characterized by scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). Electric resistance of the composites was tested using a 4-point-probe electric resistivity tester. The EMI-SE of the composites was evaluated by means of the reflection and adsorption methods. From the results, it was found that the EMI-SE of the composites enhanced with increasing Ni plating time and content. In high frequency region, the EMI-SE didn`t show further increasing with high Ni content (Ni-CF 10 min) compared to the Ni-CF 5 min sample. In conclusion, Ni content on the carbon fibers can be a key factor to determine the EMI-SE of the composites, but there can be an optimized metal content at a specific electromagnetic frequency region in this system.

본 연구에서는 니켈 함량에 탄소섬유강화 에폭시 기지 복합재료의 전자파 차폐효과에 대해 고찰을 위해 탄소섬유 표면에 시간의 변수에 따른 무전해 도금을 실시하였다. 탄소섬유 표면의 특성은 주사전자현미경과 X-선광전자분광법으로 측정하였고 전기적 특성은 4단자법으로 분석을 진행하였다. 복합재료의 전자파 차폐효과는 흡수와 반사 두 가지 방법으로 분석을 진행하였다. 실험 결과로부터 전자파 차폐효과는 탄소섬유 표면에 코팅된 니켈 함량이 증가됨에 따라 순차적으로 증가되는 것이 확인되었으나, 고주파 영역에서는 과량의 니켈 도금이 더 이상의 전자파 차폐효율을 증가시키지 않는 것이 확인되었다. 결론적으로 니켈 함량이 탄소섬유 복합재료의 전자파 차폐효과를 결정하는 요소가 될 수 있다고 판단되나, 특정 주파수마다 최적화된 금속도입 함량에 대한 변수가 있을 수 있다고 판단된다.