It was performed to test the combustive properties of low density polyethylene and ethylene vinyl acetate (LDPE-EVA) mixture by the addition of magnesium hydroxide. Flame retardant of natural magnesium hydroxide was added to the mixture of LDPE-EVA in 40 to 80 wt% concentration. The composite was compounded to prepare specimen for combustive analysis by cone calorimeter (ISO 5660-1). Comparing with virgin LDPE-EVA, the specimens including the magnesium hydroxide had lower combustive properties. It is supposed that the combustion-retardation properties in the composites improved due to the endothermic decomposition of magnesium hydroxide. The specimens with magnesium hydroxide showed both the lower peak heat release rate (PHRR) and lower effective heat of combustion (EHC) than those of virgin polymer. As the magnesium hydroxide content increases, time to ignition increased and the peak heat release rate decreased.

수산화마그네슘이 첨가된 저밀도 폴리에틸렌-에틸렌 비닐 아세테이트 혼합물의 연소성을 시험하였다. 저밀도 폴리에 틸렌-에틸렌 비닐 아세테이트에 수산화마그네슘을 40∼80 wt% 첨가하여 용융 혼합하고 성형 후 콘칼로리미터(ISO 5660-1)를 이용하여 그의 연소성을 시험하였다. 수산화마그네슘을 첨가한 시험편은 첨가하지 않은 시험편에 비하여 그의 연소성이 감소하였다. 이것은 순수한 저밀도 폴리에틸렌-에틸렌 비닐 아세테이트에 첨가한 수산화마그네슘의 흡열 분해 때문에 연소 억제성이 향상된 것으로 생각된다. 수산화마그네슘을 첨가한 시험편은 첨가하지 않은 시험편 에 비해 낮은 최대열방출률과 낮은 유효연소열을 나타내었고, 수산화마그네슘 함량이 증가할수록 착화시간은 길어지 고, 최대열방출률은 감소하였다.