Polysulfone (PSf) membranes were prepared via the phase inversion process. Polyvinylpyrrolidone (PVP) was added as a nonsolvent additive in the casting solution containing a mixture of PSf and n-methylpyrrolidone. The added PVP played a role of enhancing liquid-liquid phase separation of the casting solution, and significantly reduced the solution fluidity. When prepared via the diffusion-induced process using water as a precipitation nonsolvent, the solidified membranes revealed a typical asymmetric structure irrespective of the addition of PVP. With 5 wt% PVP content, the finger-like cavities were more developed in the membrane sublayer compared to that of the membranes prepared without PVP. In contrast, with more than 10 wt% of PVP, the formation of finger-like cavities was suppressed, and the thickness of polymer nodule layer was increased. The surface porosity was also increased with the PSf content in the casting solution. The water permeability curve as a function of PVP addition revealed the inflection point. The maximum water permeability for 12 wt% PSf membrane was obtained with 5 wt% PVP content, and that for 18 wt% PSf membrane with 15 wt% PVP.

상전환법을 이용하여 폴리설폰, n-메틸피롤리돈과 폴리비닐피롤리돈으로 이루어진 제막용액으로부터 고분자 분리막이 제조되었다. 폴리비닐피롤리돈은 폴리설폰에 대한 고분자 첨가제로서 제막용액에 첨가되었으며, 침지용 비용매로는 물이 사용되었다. 첨가된 폴리비닐피롤리돈은 제막용액의 열역학적 상분리를 촉진하는 역할을 할 수 있음을 보였으며, 유동성을 급격히 감소시키는 특성을 보였다. 제조된 막들은 전형적인 비대칭성 구조를 보이며, 첨가제 없는 경우와 비교하였을 때 폴리비닐피롤리돈 함량이 5 wt%가 첨가된 경우 모두 손가락 기공이 약간 더 크게 나타났으며, 10 wt% 이상에서 손가락 기공의 크기가 줄고 표면 고분자 알갱이층의 두께가 뚜렷하게 증가하는 것으로 나타났다. 동일한 폴리비닐피롤리돈 함량에서는 폴리설폰의 함량이 높을수록 손가락 기공의 형성이 시작되는 곳이 표면으로부터 멀리 떨어지는 것으로 나타났다. 표면기공도는 고분자 첨가제를 포함하지 않고 제조된 막의 경우 폴리설폰 함량이 낮을수록 기공도가 크게 나타났다. 폴리설폰 함량이 같을 때 물투과도는 폴리비닐피롤리돈의 함량 증가에 따라 선형으로 변하지 않고 변곡특성을 보였다. 폴리설폰 함량 12 wt%에서 최대 물투과도는 폴리비닐피롤리돈 5 wt%이었을 때 나타났으나, 폴리설폰 함량이 18 wt%이었을 때 최대 투과도는 폴리비닐피롤리돈 함량이 15 wt%일 때 나타났다.