The aqueous solution of Sunset Yellow-FCF (SY-FCF) began to show schlieren texture at room temperature when its concentration reaches 25 wt%. A further increase of the concentration of SY-FCF to 28wt% resulted in a perfect nematic liquid crystal phase. However, more than 30wt% of SY-FCF in aqueous solution was required to make an optically anisotropic film simply by shear coating. In our study, concentration of SY-FCF solution, coating speed, drying temperature, and relative humidity were considered as coating parameters affecting the preparation of optically anisotropic thin films. From analysis of variance analysis (ANOVA), the solution concentration was revealed as a main factor affecting the film thickness. The drying temperature and solution concentration were main factors affecting the transmittance of parallel direction (To). Especially, SY-FCF aqueous solution with high concentration induced a better alignment of LC columns and produced highly oriented anisotropic films. In this study, optically anisotropic films prepared by 33wt% of SY-FCF in aqueous solution showed 89.7~ 98.7% of degree of polarization.

자기 조립성 염료인 Sunset Yellow-FCF 수용액은 상온에서 농도 25wt%부터 schlieren 구조의 액정상을 보이기 시작하여, 28wt% 이상이면 완전한 네마틱 액정상으로 관찰되었다. 전단배향에 의한 코팅으로 광학적 이방성 필름을 제조하기 위해서는 30wt% 이상의 농도가 필요하였다. 액정 색소의 농도, 코팅속도, 건조 온도, 상대습도 등 코팅 변수가 최종 박막필름의 두께, 투과도에 미치는 영향 분석에 의하면, 최종 필름의 두께에는 용액의 농도가 가장 큰 영향을 주었으며, 평행방향의 투과도에는 건조 온도와 농도의 영향이 가장 컸다. 특히 Sunset Yellow-FCF의 농도 증가로 전단코팅에 의한 배향성이 개선되고 높은 편광도를 갖는 필름제조가 가능하였다. 본 실험에서는 33wt%의 Sunset Yellow-FCF 수용액을 사용하면, 89.7~98.7%의 편광도를 갖는 광학적 이방성 필름이 제조되었다.