the Heck coupling reaction between 4,7-Di-thiophen-2-yl-benzo(1,2,5)thiadiazole and 1,4-bis(dodecyloxy)-2,5-divinylbenzene. The maximum absorption and band gap of PPVTBT were 550 nm and 1.74 eV, respectively. The HOMO and LUMO energy level of PPVTBT were -5.24 eV and -3.50 eV, respectively. The photovoltaic device based on the blend of PPVTBT and (6)-1-(3-(methoxycarbonyl)propyl)-{5}-1-phenyl[5,6]-C61 (PCBM) (1 : 6 by weight ratio) was fabricated. The efficiency of device was 0.16%. The short circuit current density (Jsc), fill factor (FF) and open-circuit voltage (Voc) of the device was 0.74 mA/cm2, 31% and 0.71 V, respectively, under AM 1.5 G and 1 sun condition (100 mA/cm2).

4,7-Di-thiophen-2-yl-benzo(1,2,5)thiadiazole과 1,4-bis(dodecyloxy)-2,5-divinylbenzene을 Heck coupling 중합법을 이용하여poly[4,7-Di-thiophen-2-yl-benzo(1,2,5)thiadiazole]-alt-1,4-bis(dodecyloxy)-2,5-divinylbenzene (PPVTBT) 공중합체를 합성하였다. 합성한 PPVTBT의 최대흡수파장과 band gap은 각각 550 nm와 1.74 eV이고 HOMO와 LUMO enegry level은 각각-5.24 eV, -3.50 eV로 나타났다. 합성한 공중합체인 PPVTBT와 (6)-1-(3-(methoxycarbonyl)propyl)-{5}-1-phenyl[5,6]-C61(PCBM)을 1 : 6의 중량비로 blend하여 제작한 소자의 효율은 AM 1.5 G, 1 sun 조건(100 mA/cm2)에서 0.16%의 효율을 보였다. 그리고 소자의 Jsc (short circuit current), FF (fill factor)와 Voc (open circuit voltage)는 각각 0.74 mA/cm2, 31%,0.71 V로 나타났다.