Photodegradation characteristics of polyolefin composites were studied. Thermogravimetric analysis results suggest that the polyolefin blends used in this study have different amounts of talc. The mechanical behaviors of polyolefin blends, which experienced UV-irradiation in accordance with SAE J1960, are investigated using tensile and Izod impact tests. These results show that as the UV-exposure time increases, a significant drop in the elongation at break and impact strength at a low temperature are observed. This may be explained by the decreases in elastic energy derived from the scission of polymer molecular chains and the low density of entanglement after UV- photodegradation. Scanning electron microscopy observations indicate that no crack and surface damage are observed, while the additional talc particles are exposed, on the UV-exposed surfaces. The exposure of talc particles may be responsible for the discoloration of UV-exposed polyolefin blend surface. Observation using Fourier transform infrared spectroscopy (FT-IR) confirms the presence of photodegradation on the surface of UV-exposed polyolefin blend.

폴리올레핀 복합소재의 UV 광열화 특성을 조사하였다. 열중량분석 결과, 3종의 폴리올레핀 복합소재는 서로 다른 talc 함유량을 가지고 있음을 확인하였다. SAE J1960 규격에 따라 UV 조사된 폴리올레핀 복합소재의 기계적 거동을 관찰하기 위해 인장시험 및 아이조드 충격 시험을 수행하였다. UV 노출 시간이 증가함에 따라 연신율과 저온 충격강도는 급격히 감소하였다. 이는 UV 광열화에 의한 폴리머 분자체인의 절단 및 얽힘 밀도 감소에 따른 탄성력의 감소에 기인한 것으로 보인다. 전자주사현미경 관찰을 통하여 UV 조사 후 표면상에 크랙이나 표면손상은 존재하지 않았지만, UV 노출에 따른 추가적인 talc 입자의 표면 노출을 관찰할 수 있었다. 이러한 talc 입자의 표면 노출은 폴리올레핀 복합소재의 변색 원인으로 추정된다. 적외선분광분석을 통하여, UV 조사된 폴리올레핀 복합소재의 표면상에 광열화가 진행되었음을 확인하였다.