A basic objective is the preparation and surface studies of supported molten salt catalysts because molten salts can stay as the liquid phase in the range of the ordinary reaction temperature. Many kinds of metal salt mixtures for the formation of molten salt phase are appliable but CuCl and KCl were selected in this study because Cu is considered catalytically reactive in many reactons. The loading of the molten salt was selected as 25 vol% of the total pore volume of γ-alumina to provide reasonable exposed surface area. The surface structure of catalysts containing molten salts in the γ-alumina was studied using scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS). CuCl and KCl were added into the γ-alumina using concentrated hydrochloric acid solution by the impregnation technique. The surfaces of the prepared catalysts before and after heat treatments were compared and they suggested that the heat treatment of catalysts helped the formation of molten-salt although the surface compositions of CuCl and KCl were not uniform.

비균일계 촉매의 일반적인 형태는 촉매로서 활성이 있는 금속 혹은 금속 화합물을 표면적이 넓은 다공성 물질인 지지체에 분산 담지시켜서 금속의 표면적을 높이고 이로부터 금속의 분산이 높아지면서 촉매로서의 활성도 높아져 일반적인 반응에 응용되고 있다. 그러나 본 연구에서는 금속염을 이용한 액상 촉매의 제조 및 응용에 초점을 맞추었다. 일반적인 금속염들은 높은 온도에서도 용융되지 않지만 이 금속염 화합물에 다른 금속염 화합물을 함께 섞어 혼합시키면 이 혼합물이 보통의 비균일 촉매 반응온도인 200 ℃에서 400 ℃의 범위에서 액상으로 존재할 수 있게 된다. 고온에서 액상형태가 되는 용융된 금속염 혼합물(molten salt)을 지지체의 세공 내에 담지시켜 담지된 액상 촉매로서의 가능성을 알아보고 이들의 촉매 제조와 표면 연구에 초점을 맞추었다. 이들 금속염 혼합물은 종류가 매우 다양하여 여러 종류의 금속에 대하여 혼합염을 선택하여 응용할 수 있다. 본 연구에서는 일반적인 촉매로 많이 이용되고 있는 구리를 선정하고 이의 염화물인 염화구리(CuCl)와 함께 혼합되어 용융될 수 있는 금속염 혼합물을 만들기 위해 칼륨 염화물을 선택하여 CuCl-KCl 혼합염을 촉매 제조에 이용하였다. 이 금속염 혼합물을 지지체에 첨가시킨 양은 담지 시킬 알루미나 세공 부피의 약 25%로 하여 용융된 금속염의 표면적이 넓어지도록 하였고 제조 후의 표면은 SEM와 EDS를 이용하여 분석하였다. 금속염 혼합물은 염산 수용액을 이용하여 함침법으로 담지 시켰으며 제조한 직후와 제조한 후 금속염 혼합물을 용융점 이상으로 3 h 동안 열처리 한 후의 표면을 비교하였다. 실험 결과 표면에서의 CuCl-KCl의 조성은 일정하지 않았지만 이 열처리가 표면에서 금속염 혼합물의 형성을 촉진시키고 있음을 알 수 있었다.