Research Papers : Asymmetric Catalytic Activity of Mesoporous Mordenite containing Polymeric Chiral Salen Complexes in the Mesopore System

Xiao Feng Guo

Abstract

The formation of mesoporous pores in the microporous mordenite crystals was performed by controlled silica extraction on alkaline treatment. Inner tunable mesopore size could be controlled by changing the concentration of alkaline solution. The pore structure of mordenite zeolite was studied by instrumental analysis after alkaline-treatment. To obtain the cage type mesopores, Ti-coating on the ourside mordenite crystals before alkaline treatment was investigated to be the most effective. Polymeric chiral salen Co (III) complexes were successfully encapsulated in mesoporous mordenite zeolite by “ship-in-a-bottle” method. The heterogeneous catalyst could be applied in asymmetric ring opening of epichlorohydrine by water. It showed very excellent enantioselectivity with a high yield in the catalysis.

연구논문 : 폴리머 키랄 살렌을 함유한 메조세공 모더나이트의 비대칭 촉매 활성

곽소붕,김용석

초록

모더나이트결정 중의 실리카를 제어된 알칼리용액의 처리로 추출제거하여 중간세공이 형성되도록 하였다. 형성된 중간세공의 크기는 알칼리용액의 농도를 변화시킴으로써 조절할 수 있었다. 알칼리처리 후의 모더나이트 제올라이트 내부의 세공구조를 조사하였다. 새둥지형태의 중간세공을 형성시키기 위해서는, 알칼리용액 처리전에 모더나이트결정의 바깥표면을 티타니아로 코팅하는 것이 가장 효과적임을 관찰하였다. 모더나이트 내부의 중간세공에 고분자형의 코발트(III) 살렌착체를 “ship-in-a-bottle”법으로 가둔 촉매를 제조하였다. 이 고정화촉매를 물에 의한 에피클로로히드린의 산소고리열림반응에 사용하여, 촉매반응에서 높은 수율과 광학선택성을 얻을 수 있었다.