The deactivation of V/TiO2 catalyst used in SCR (Selective Catalytic Reduction) using ammonia as a reductant to remove the nitrogen oxides (NOx) in the exhaust gas from fired power plant has been studied. The activity and surface area of the catalyst (Used-cat) which was exposed to the exhaust gas for long period have considerably decreased. The characterizations of these SCR catalysts were performed by XRD, FT-IR, FE-SEM, and IC/ICP. The crystal structure of TiO2 both fresh and used catalyst has not been changed. However, (NH4)HSO4 deposited on the used catalyst surface verified from FT-IR, FE-SEM, and IC/ICP analysis. Moreover, the durability of SO2 was increased by diminishing sulfate (SO4-2)f form.

화력 발전소에서 발생되는 질소산화물(NOx)을 제거하기 위하여 환원제로써 NH3를 이용한 선택적 촉매환원법(Selective Catalytic Reduction: SCR)에 사용되는 V/TiO2 촉매의 활성저하에 관하여 연구하였다. 장기간 배기가스에 노출된 촉매 (Used-cat)의 활성과 비표면적이 상당히 감소되었다. 촉매의 특성분석은 XRD, FT-IR, FE-SEM, IC/ICP 등을 이용하여 수행 하였다. 분석결과 배기가스에 노출되지 않은 사용 전 촉매(Fresh-cat)와 사용 후 촉매(Used-cat) 두 촉매 모두 TiO2의 결정구조는 변하지 않았다. 그러나, FT-IR, FE-SEM, IC/ICP에 의한 촉매의 특성분석결과 사용 후 촉매(Used-cat) 표면에 (NH4)HSO4가 침적이 되었음을 확인하였다. 또한, SO2에 대한 내구성이 우수한 촉매일수록 표면에 형성되는 황산염(SO4-2)이 적게 형성됨을 확인할 수 있었다.