Herein, we synthesized silica-coated chrome yellow particles having improved chemical resistance. The intermediate with a good dispersion stability was prepared and the chemical resistance of the final product was investigated. The effects of pH and temperature, as the main parameters influencing the formation of particles, the reduced particle size by homogenizer on the silica coating were investigated. The change in the particle morphology by temperature and pH was also studied. As the results, small and monodisperse particles were achieved at low pH and high temperature. Good silica coating was obtained when used reduced size of the particles by homogenizer. Furthermore, the sufficient silica coating by microencapsulation was obtained at 9 10 pH and the temperature above 90 .

본 연구에서는 실리카 코팅을 통하여 높은 내약품성을 갖는 황연입자를 제조하였다. 합성 과정에 수중 분산도 향상을 위한 중간체 제조의 최적화와 제조된 실리카로 코팅된 황연입자의 내약품성을 조사하였다. 합성과정에서 입자 생성에 가장 영향이 높은 변수인 pH와 반응온도에 따른 입자경의 변화를 관찰하였으며, homogenizer 이용하여 변화된 입자경에 따른 실리카 코팅에의 영향, 코팅 후 온도 및 pH의 변화에 따른 입자형상의 변화를 관찰하였다. 실험 결과로, 황연안료의 합성공정에서 생성용액의 pH가 낮을수록 합성 및 숙성온도가 높을수록 작고 균일한 입자를 얻을 수 있었다. 황연입자의 코팅 전 입자경이 작을수록 실리카 코팅이 우수하였다. 또한 충분한 마이크로캡슐화에 의한 실리카 코팅은 pH 9 10 및 반응온도 90 이상에서 얻을 수 있었다.