For the synthesis of lead chromate pigments, we investigated the characteristics of particle growth with reacting conditions in the synthetic process, the effect of additives, and its micro-capsulation. The more tiny and uniform dispersion particles could be obtained at a lower pH and diluter intial concentration. The variation range of average pigment size was increased with the agitating speed. The pigment size could be controlled by adding aluminum sulfate as an additive, which maintained the optimum particle dispersion. It was found that the optimum micro-capsulation conditions were pH 9 10 and above 90 during the micro-capsulation of lead chromate pigment, and below 0.5% humidity after micro-capsulation.

크롬산납안료입자의 합성과정에서 반응조건의 변화에 따른 입자의 성장특성, 첨가제 첨가에 의한 영향, 그리고 마이크로캡슐화에 관하여 조사하였다. 크롬산납 무기안료의 합성과정에서 생성용액의 pH가 낮을수록, 반응물질의 초기농도가 묽을수록 입자크기가 작은 균일한 분산입자를 얻을 수 있었다. 교반속도가 큰 경우에서 평균입자크기의 감소 및 증가에 대한 변화폭이 크게 나타남을 알 수 있었다. 합성된 크롬산납 안료입자의 숙성과정에 황산알루미늄을 첨가하여 표면처리 함으로써 입자크기의 제어가 가능하였고, 입자의 입도분포 상태를 최적 분산 상태로 유지하는 효과가 있음을 알 수 있었다. 안료입자의 마이크로캡슐화가 진행되는 용액의 pH 범위를 9 10, 반응온도를 90 이상으로 유지하고 마이크로캡슐화 후 충분한 건조를 통해 입자의 수분함량을 0.5% 이하로 유지할 때 최적의 마이크로캡슐화가 됨을 알 수 있었다.