This research was conducted to evaluate the effect of lignin addition on the characteristics of portland cement pastes. Lignin was added to cement at the ratio of 0.5 to 2.0% on dry weight basis. The specimens were cured for 3, 7, 14, and 28 days. Distilled water and sea water were used as leaching solutions. pH and concentration of Ca, Na, and K ions in the leaching solutions were analyzed. Lignin addition of 0.5∼2.0% to cement pastes decreased the leached concentration of Ca, Na, and K ions for distilled water, compared to the case without lignin addition. However, a significant pH variation of the leached solutions was not observed with the lignin addition. Lignin addition significantly improved the compressive strength of cement pastes, approximately 30∼60% for curing in distilled water and 3∼20% for that in sea water.

본 연구는 리그린을 포틀랜드시멘트에 첨가하였을 때 시멘트 페이스트의 특성에 미치는 영향을 평가하고자 실시하였
다. 시멘트 질량에 대하여 리그닌을 0.5∼2.0%의 비율로 첨가하였으며, 각각 3, 7, 14, 28일간 공시체를 양생하였다.
용출용액으로는 초순수(超純水)와 해수(海水)를 사용하였으며, 양생기간 별로 pH 및 Ca, Na, K의 용출농도를 측정하
였다. 시멘트의 물리적 특성으로 압축강도를 측정하였다. 이온 성분의 용출농도는 초순수에서 리그닌을 첨가하였을
때 리그닌을 첨가하지 않은 경우 보다 다소 낮게 나타났다. 리그닌을 0.5∼2.0% 첨가한 경우를 첨가하지 않은 경우와
비교하였을 때 리그닌 첨가가 용출용액의 pH에는 큰 영향을 미치지 못하였다. 리그닌을 0.5∼2.0% 첨가한 경우 시멘
트의 압축강도는 초순수 양생에서 30∼60%, 해수 양생에서는 3∼20% 정도 증가하여 물리적 특성이 크게 개선되었다.