Siloxane monomer and oligomer were introduced to n-butyl acrylate and methyl methacrylate copolymer for improvement of water resistance and tactile sensation of acryl-type emulsion. Terpolymerimerization of n-butylacrylate, methyl methacrylate and siloxane monomer or oligomer was carried out in aqueous solution. The glass transition temperature (Tg) of terpolymer decreased with increasing siloxane monomer, however, the Tg of terpolymer increased with increasing siloxane oligomer due to the crosslinking of acrylated end group. The adhesion property and surface energy of the obtained terpolymer decreased with introducing siloxane monomer or oligomer in terpolymer. Decrement of tack and surface energy means the enhancement of water resistance and tactile sensation of the emulsion.

아크릴계 에멀젼의 내수성 및 촉감을 향상시키기 위해 유연하고 낮은 표면에너지를 가지는 실록산 단량체 및 올리고
머와의 공중합체를 제조하였다. 아크릴 작용기를 갖는 실록산 단량체와 올리고머를 합성하고, n-butyl acrylate와 methyl
methacrylate를 사용하여 실록산 함유 아크릴 삼원공중합체를 제조하고 표면자유에너지의 변화 및 점착특성을 조사
하였다. 삼원공중합체의 Tg는 실록산 단량체의 주입 양이 증가함에 따라 감소하였으나, 올리고머의 경우는 양 말단의
아크릴기에 의해 가교반응이 일어남으로써 삼원 공중합체의 Tg는 증가하였다. 실리콘 단량체와 올리고머를 첨가함에
따라 tack 값과 표면에너지가 감소하는 것으로 내수성 및 촉감이 향상된 것을 확인하였다.