The alternate plating method was suggested by a tin-cobalt alloy plating process which has excellent mechanical characteristics and also favorable to environment. Tin-cobalt alloy plating has many advantages such as nontoxicity, variable color-tone, and no post-treatment process. In this study, the plating conditions such as temperature, pH, current density, plating time, andamount of additive (glycine) were determined in the tin-cobalt alloy plating process through Hull-cell test and surface analysis. As the result of Hull-cell analysis, brightness became superior as the amount of glycine increased. It was found that the optimum alloy ratio was 0.03 M of SnCl22H2O and 0.05 M of CoSO4 7H2O at 50℃, pH 8.5, and 0.5 A/dm2. The optimum amount of additive was 15 g/L of glycine and 0.1 g/L of organic acid. Then, the solution including glycine was recommended as an optimum plating solution for a chromium plating process.