Non-halogen flame retardants have been the focus of extensive research because of environmental problems. Hexakisphenoxycyclotriphosphazene was synthesized in order to use as the flame retardant of ABS resin. And using bisphenol A, the polymers containing a cyclotriphosphazene structure were synthesized in order to also use as the flame retardant of ABS resin. All of the synthesized polymers themselves had the excellent flame retardancy. And as their molecular weight and crosslinking density were increased, the thermal stability was increased. But when the synthesized compounds were used as the flame retardant for ABS resin, the lower molecular weight compound in these compounds showed the better flame retardancy and the better physical properties of ABS resin.

환경적인 문제로 인하여 할로겐 원소를 갖지 않는 난연제에 대한 연구가 매우 활발하다. 본 연구에서는 hexakisphenoxycyclotriphosphazene을 합성하였으며, 이것을 ABS 수지의 난연제로 사용하여 보았다. 그리고 bisphenol A를 이용하여 cyclotriphosphazene구조를 갖는 분자량이 큰 화합물들을 합성하여 이들을 역시 ABC 수지의 난연제로 사용하여 보았다. 합성한 고분자들 자신은 매우 우수한 난연성을 보여주었으며 분자량이 커지고 가교구조가 많아질수록 열적 안정성은 더 높아졌다. 그러나 이러한 화합물들을 ABS 수지의 난연제로 사용하였을 때 이들 화합물들 중에서 비교적 분자량이 낮은 화합물이 ABS 수지에 더 우수한 난연성을 나타내게 하였으며 ABS수지의 물리적인 성질도 더 우수하게 하였다.