The water-soluble defoamers were fabricated by the mixing polyol, modified silicon resin, silicon resin and surfactant. For the defoamers, the various properties such as phase-separation time, viscosity and defoamerability were examined. The phase-saparation time of PPG mixtures was found to be PPG 400>PPG 3,000>PPG 1000. When PPG 1000 was mixed, mixtures represented the excellent defoamerability The phase-saparation time of silicon resin mixtures was TSF-451-350>TSF-451-200>TSF-451-50. As more of high molecular silicon resin was mixed, the resulting mixtues showed reduced defoamerability. When the TSF-451-50 was mixed, the mixture's volume was increased because of the reduction of solubility. The modified silicon resin was smoothly dispersed in water, but the compatibility with PPG was not good. The defoamerability of surfactant was SPAN 20>SPAN 60>SPAN 80. SPAN 80 showed good miscibility for the silicon resin, but not good for YAS 6406 or PPG 1000.

폴리올, 실리콘 수지, 변성 실리콘 수지 등을 유화제로 유화시켜 수용성 소포제를 제조하였다. 제조한 소포제에 대하여 소포성, 상분리 시간, 점도 등을 측정하였다. PPG 혼합물의 상분리 시간은 PPG 400>PPG 3000>PPG 1000이었다. PPG 1000을 혼합하였을 때는 다른 것에 비하여 뛰어난 소포성을 나타내었다. 실리콘 수지 혼합물의 상분리 시간은 TSF- 451-350>TSF-451-200>TSF-451-50이었다. TSF-451-50을 혼합하였을 때는 상용성 부족으로 혼합물의 부피가 증가되었다. 고분자량의 실리콘 수지를 사용할수록 소포성은 좋지 않았다. 변성 실리콘 수지는 물에 잘 분산되었지만 폴리올에 대한 상용성은 좋지 않았다. 유화제에 대한 소포성은 SPAN 20>SPAN 60>SPAN 80의 순이었다. SPAN 80은 실리콘 수지에 대하여 혼합성이 좋지 않았지만 YAS 6406이나 PPG 1000에 대해서는 좋은 혼합성을 나타내었다.