Vanadium pentoxide xerogels with a doping ratio of AL/V2O5 ranging from 0.01 to 0.05 were synthesized by doping Al into V2O5 xerogel via the sol-gel process. By using the synthesized AlxV2O5. the Li/AlxV2O5 cells were assembled to investigate the chemical and electrochemical properties. Surface morphology of the AlxV2O5 xerogel showed an anisotropic corrugated sheet-like matrix, and the interlayer distance was about 11.5 Å. The IR spectra of the AlxV2O5 xerogels showed enhanced reversibility and energy density compared with the V2O5 xerogel. the specific capacity of the Al0.05V2O5 xerogel was more than 200 mAh/g at 10 mA/g discharge rate, and cycle efficiency was about 90% after the 31st cycling test between 1.9 V and 3.9 V.

Al이 0.01에서 0.05 몰 도핑된 오산화바나듐을 졸-겔법을 이용하여 제조하였고, Al이 도핑된 오산화바나듐의 화학적성질과 전기화학적 특성을 조사하기 위하여 Li/AlxV2O5 전지를 만들었다. AlxV2O5 xerogel의 표면형상은 비둥방성의 주름진 판상을 이루며 층간거리는 약 11.5 Å이었다. IR 스펙트럼에 의하면 도핑된 Al이 V2O5의 vanadyl기에 결합하고 있는 것으로 나타났다. AlxV2O5 xerogel은 가역성과 에너지밀도가 V2O5보다 향상되었다. 또한 10 mA/g의 방전율로 얻은 Al0.05V2O5 xerogel의 비용량은 200 mAh/g 이상이었으며, 1.9 V에서 3.9 V 전위영역에서 31회의 연속 충방전 실험을 한 결과 약 90%의 사이클효율을 나타내었다.