In this study, nano sized colloidal Ag was made by using a seed sol method. Colloidal Ag solution was spouted on the surface of the inorganic pigment using the hybridizer system and spray nozzle. Then, the surface of the inorganic pigment was modified by TiO2 to obtain the antibacterial ability. In the manufacturing process of nano sized colloidal Ag, it was confirmed that the size of particles increased by addition of AgNO3 and increased the reaction time. The antibacterial measurement of the inorganic pigment showed that the growth of fungus decreased as the reaction time was increased. After the antibacterial ability appeared, in 5~7 h of the antibacterial inoculation experiment, it was measured that the antibacterial activity was excellent at a fixed time frame. The photodecomposition of benzene using TiO2 as the photocatalyst showed 60~70% efficiency in about 80 min. reaction time. It was shown that more than 90% of this efficiency was achieved in the reaction time of about 30 min.

본 연구에서는 seed sol 부가법을 통해 나노 사이즈의 콜로이달 Ag를 제조하였다. 제조된 콜로이달 Ag 용액은 hybridizer system과 spray nozzle을 통하여 제지용 무기안료 표면에 분사한 후 이산화티탄으로 표면개질하여 기능성 항균 복합 분체를 제조하였다. 나노 사이즈의 콜로이달 Ag 제조에 있어 AgNO3의 첨가와 시간의 경과에 따라 흡수도가 커지는 것으로 단위 중량당 입자의 크기가 커짐을 확인할 수 있었다. 제조된 기능성 무기안료의 항균성 측정은 균들의 해당 균주에서 시간이 증가함에 따라 균의 성장이 억제되는 결과를 나타내었고 항균접종 실험 실시 후 5~7 h 안에 항균성이 발현되면서 일정한 시간 범위 내에서의 항균력이 우수한 것으로 측정되었다. 또한 TiO2의 광촉매 효과 측정 결과 benzene의 광분해 효율실험에서 반응시간 80 min 동안 60~70% 정도의 효율을 보였고, 반응시간 30 min 정도에서 이미 달성한 분해효율이 90% 이상에 도달해 있음을 알 수 있었다.