In this work, NaA type zeolite of fine crystal less than 0.5 μm was synthesized by controlling crystallization and aging time. NaA type zeolite membranes were prepared using a conventional hydrothermal method and clear solution method followed by characterization of permeation and separation factor. Especially submicron size zeolite powder was used as seed material on the alumina support and the temperature of synthesis was fixed at 80 ℃. It was confirmed that the prepared zeolite membrane using clear solution method was more uniform compared to the hydrothermal synthesis. The zeolite membrane thickness of ca. 10 μm was obtained. And the zeolite membrane had the separation property of 65% as permeating 50% methanol mixed solution.

본 연구에서는 결정화시간 및 숙성시간을 조절하여 0.5 μm 이하의 미립결정을 갖는 NaA형 제올라이트를 합성하였다. 합성된 NaA형 제올라이트를 이용하여 알루미나 지지체 표면에 첨착하여 수열합성법과 희석용액법으로 제올라이트박막을 형성시켰으며, 제올라이트 막의 투과도와 분리능을 분석하였다. 특히 희석용액법에서는 미립 제올라이트 분말을 seed로 활용하여 합성온도를 80 ℃에서 반응시간을 조절하여 실험하였다. 실험결과 기존의 수열합성법에 비하여 희석 용액법으로 제조한 제올라이트 박막이 보다 더 균일하게 형성되었음을 확인할 수 있었으며, 10 μm 두께의 박막을 얻었다. 합성된 제올라이트 박막에 50% 메탄올 혼합용액을 투과하여 65%의 분리성능을 나타내었다.