Acryl resin was mixed with materials such as filler, defoamer, thickener and curing agent. Then epoxy resin was mixed with the materials such as filler, defoamer, and thickener. The acryl mixtures and the epoxy mixtures were blended together in 0~50 wt%. For the blends, the various properties such as viscosity, drying time, hardness and water-resistance were experimentally tested. With the increasing of epoxy mixtures, it showed enhensed properties in the hardness, adhesive strength and water-resistance. When the curing promoter was added to the mixtures, it induced shorter pot-life and faster drying time. With the more loading of filler, the adhesion was gradually increased, but was conversely decreased over 130 phr. With added thickener, adhesion was gradually increased, but the adhesive strength and the water-resistance were proportionally decreased. The guarantee of three months for the water-resistance could be obtained by blending epoxy mixtures over 30 wt%

아크릴 에멀젼 수지와 에폭시 라텍스에 충전재, 소포제, 증점제, 경화촉진제 등을 각각 분산시켜 아크릴 수지 혼합물과 에폭시 수지 혼합물을 만들었다. 아크릴 수지 혼합물에 에폭시 수지 혼합물을 0~50 wt% 범위 안에서 혼합하여 점도, 건조시간, 경도, 내수성 등 여러 가지 물성을 측정하였다. 에폭시 혼합물의 양이 늘어날수록 경도와 접착강도 및 내수성은 높은 값을 나타내었다. 경화촉매가 첨가됨에 따라 혼합물은 보다 짧은 건조시간과 가사시간을 나타내었다. 충전재의 함량이 늘어날수록 부착력은 점차 증가하였지만 충전재 함량 130 phr 이상에서는 오히려 감소하였다. 증점제의 함량이 늘어날수록 접착력은 증가하였지만 충전재 함량 130 phr 이상에서는 오히려 감소하였다. 증점제의 함량이 늘어날수록 접착력은 증가하였지만 접착강도와 내수성은 상대적으로 감소하였다. 적어도 3개월의 내수성을 갖기 위해서는 에폭시 혼합물을 30 wt% 이상 혼합해야 한다.