Barium ferrite was prepared from a mixed solution of Ba(NO3)2, Fe(NO3)3·9H2O and KOH by the hydrolysis and dehydration through hydrothermal treatment. The characteristics of the barium ferrite, formed in the batch reactor were investigated thru varying the Fe/Ba molar ratio and reaction time in the respective range of 1 ~ 12 and 30 ~ 360 min. Final product obtained was single-phase barium ferrite with a size of 0.3 ~ 1 μm. The maximum saturation magnetization and coercivity of the obtained powder were about 51.36 emu/g and 1355 Oe, respectively. compared with the conventional hydrothermal synthesis method, the method using supercritical water remarkably reduced the reaction time for the synthesis of barium ferrite.

Ba(NO3)2, Fe(NO3)3·9H2O 및 KOH 수용액을 사용하여 수열합성조건에서의 가수분해와 탈수반응을 통해 Barium ferrite를 합성하였다. 회분식 반응기를 이용하여 반응조건을 각각 Fe/ba 농도비는 1에서 12로 변화시켰으며, 반응시간은 30 min에서 360 min까지 변화시키면서 합성된 입자의 형태 및 조성과 자기특성에 대해서 고찰하였다. 생성된 입자는 단일상의 barium ferrite로 육각판상의 형태를 갖고 있으며, 입자의 크기는 0.3 ~ 1 μm 정도이다. 또한, 자기 특성은 최대 포화자화(σr)와 보자력(Hc)이 각각 51.36 emu/g와 1355 Oe를 가지는 barium ferrite분말을 얻을 수가 있었다. 초임계상태에서 제조된 barium ferrite는 일반적인 수열합성법으로 제조된 barium ferrite보다 빠른 시간에 안정적으로 단일상의 barium ferrite를 제조할 수 있었다.