Kinetic tests on pyrolysis of nylon-6 used in fishing net were carried out by thermogravimetric analysis (TGA) with heating rates of 0.5, 1.0, and 2.0 ℃/min, respectively. Pyrolysis started at 300 ℃, and the main region of decomposition temperature of the nylon-6 was between 360 and 440 ℃ for each heating rate. The corresponding kinetic parameters including activation energy and free exponential factor were determined by a differential method over the degree of conversions. The value of activation energies increased gradually from 128 to 433 kJ/mol as the conversion of pyrolysis reaction increased from 5% to 96%. Free exponential factor was 10^(12(-10^(21) and the slope of thermogravimetric curves was approximately linear. Nylon-6 was pyrolyzed in a micro-scale tubing bomb reactor for 60∼100 min at 440 ℃. As the reaction time increased, the yields of pyrolyzed gas also increased. The selectivity of specific hydrocarbons was not detected, and the carbon number distribution of the pyrolyzed oil was random

열중량 분석기(TGA)를 이용하여 승온속도를 0.5, 1.0 및 2.0 ℃/min으로 변화시키면서 nylon-6 재질 어망에 대한 열분해반응 특성 연구를 수행하였다. 분해반응은 300℃부터 시작되었으며, 각각의 승온속도에서 열분해반응은 360~440℃ 구간에서 급격하게 진행되었다. 미분법을 이용하여 nylon-6 재질 어망의 열분해반응 활성화에너지 및 빈도인자를 구하였다. 열분해반응 전환율이 5%에서 95%로 증가할수록 활성화에너지는 128에서 433 kJ/mol로 점진적으로 증가하였다. 열중량 변화 곡선의 기울기가 거의 직선인 구간에서 빈도인자는 10^(12)~10^(21)의 값을 나타냈다. 미분반응기에서 반응온도를 440℃로 고정한 후 반응시간을 60~100 min 동안 열분해반응 실험을 수행한 결과 반응 시간이 증가할수록 생성된 열분해 가스의 양은 증가하였다. 이때 생성된 오일의 탄소수 분포는 거의 일정하게 나타났으며, 특정한 탄화수소화합물에 대한 선택성은 나타나지 않았다.