The activities of Lanthanum (La) based metal oxide catalysts were investigated by measuring NO conversion, TPD, XRD and XPS. La was taken as a basic material at the A site. A variety of transition metals such as Cu, Fe, Mn, Co and Al, at the B site, have been studied to test the catalytic activities of NO reduction. Then, La in the A site was replaced by Ce to study the activity change. XRD and TPD bands of adsorbed oxygen were compared in view of catalytic activity of NO reduction. The catalyst replaced with Cu for B site showed high activity, and the highest activity was achieved for LaCu_0.9Mn_0.1O_3, replaced with Mn for 10% copper. The 90% La substituted catalyst by Ce (La_0.1Ce_0.9Cu_0.9Mn_0.1O_3) showed highest activity at low temperature range (200∼300 ℃). However, it showed a lower activity at higher temperature ranges.

란타늄을 기본으로 한 금속산화물 촉매 활성을 NO의 전화율, 승온 탈착(TPD), X선 회절분석(XRD) 및 X선 광전자 분광법(XPS)으로 연구하였다. La를 A site의 기본 물질로 취하였고, B site는 Cu, Fe, Mn, Co, Al 등 여러 가지 전이금속으로 치환하여 NO 환원반응에서의 촉매활성을 조사하였다. 그 다음에 A site의 La를 Ce로 치환하여 촉매 활성의 변화를 조사하였다. XRD의 흡착된 O_2의 TPD band를 NO 환원반응에서 촉매활성의 특성 관점으로 비교하였다. B site가 Cu로 치환된 촉매는 활성이 높게 나타났으며 특히 Cu의 10%를 Mn으로 치환한 LaCu_0.9Mn_0.1O_3가 더 높은 활성을 보였다. 90% La이 Ce으로 치환된 La_0.2Ce_0.9Cu_0.9Mn_0.1O_3가 저온 영역(200∼300 ℃)에서 가장 높은 활성을 나타냈으나, 고온 영역에서는 오히려 활성이 더 낮아졌다.