The crystallization behavior of an EVA/petroleum resin blend, which is commonly used as a hot melt adhesives, was investigated. Special efforts were made to explore the effects of vinyl acetate (EV) content and the petroleum tackifier on the crystallization behavior of blends. It was found that the crystallization behavior of EVA/petroleum resin blend depended strongly upon the miscibility between the two components. In the presence of petroleum resin, as a tackifier, in EVA, the crystallization rate was lowered because of a lower VA content. This was due to the interruption of EVA crystal growth by the two-phase morphology in immiscible blends. The enhancement of miscibility in blend was achieved using EVA with a higher VA content; this resulted the crystallization rate to increase. However, any further increase in the petroleum resin content, reduced the rate of crystallization. This was demonstrated by using aliphatic C5 petroleum resin, which possessed a better miscibility with EVA than C9 petroleum resin.

핫멜트 접착제의 점착 부여제로 사용되는 석유수지가 EVA/석유수지 블렌드 핫멜트 접착제의 결정화 거동에 미치는 영향을 살펴보았다. 특히, 비닐 아세테이트(VA)의 함량 그리고 점착 부여 수지의 종류가 이들의 결정화 거동에 미치는 영향을 중점적으로 고찰하였다. 순수 EVA는 VA 함량이 증가할수록 용융 온도, 용융 엔탈피가 감소하고 결정화 속도는 느려짐을 알 수 있었다. 점착 부여 수지로 사용되고 있는 석유 수지를 EVA에 블렌딩하면 이들의 결정화 속도는 EVA와 석유수지의 상용성 정도에 따라 좌우됨을 확인하였다. 상대적으로 VA함량이 낮은 EVA의 경우, 석유 수지와의 블렌딩에 의하여 상분리 현상이 발현되고 이는 EVA의 결정 성장을 방해하여 그 결과, 결정화 속도가 느려짐을 보인다. VA함량이 증가에 따른 상용성 증가는 결정화 속도를 증가시키나 무정형인 석유수지의 함량 증가로 인하여 무정형 phase 가 증가되어 결정화속도는 다시 감소되며 aromatic C9보다 상용성이 우수한 aliphatic C5 석유수지를 사용할 경우 이러한 현상이 두드러짐을 확인할 수 있었다.