Bio/photodegradable polymer composites were prepared by blending a biodegradable aliphatic polyester and a photodegradable master batch (M/B). Photodegradability, biodegradability, thermal properties and mechanical properties of the composites were investigated. The biodegradability of PBSA(polybutylene succinate adipate)/MB composites decreased with increased amount of M/B, but for PBSAT(polybutylene succinate adipate telephthalate)/MB composites, it increased. The biodegradability tests during autumn and winter showed that the tensile strength and elongation decreased slowly with increased outdoor exposure time and the amount of M/B in the composites; however, these decreased rapidly during spring and summer seasons. As the content of M/B increased, the initial mechanical properties exhibited increased deterioration, whereas the melting temperature remained unchanged

생분해성 폴리에스테르와 광분해성 M/B를 블렌드하여 생분해 및 광분해 고분자 복합체를 제조하였다. 각 조성에 대하여 광분해도, 생분해도, 열적 특성, 기계적 물성을 측정하였다. PBSAT/MB복합체의 경우 M/B의 함량이 증가할수록 생분해도가 증가한 반면에 PBSA/MB의 경우는 감소하였다. 가을과 겨울 광분해 실험에서는 노출 시간과 M/B의 양이 증가할수록 인장 강도와 신장율이 서서히 감소한 반면, 봄과 여름 실험에서는급격히 감소하였다. 또한 초기 기계적 물성은 M/B의 양이 증가함에 따라 감소하였고, 조성에 의한 용융온도는 변화가 없었다.