Carbon electrodes for fluorine electrolysis were prepared from petroleum cokes containing coal tar pitch as binder and the effects of binder contents on electrode properties were investigated. The evaluations were performed by measuring physical properties, mechanical strength, and electrochemical behavior by cyclic voltammogram in molten KF·2HF electrolyte and impedance spectroscopy in 0.5 M H2SO4. It was found that the carbon anode formed with 45 wt% coal tar pitch as the binder had hetter electrode properties compated to those with other contents. This porous carbon anode showed a high critical current density of 12.07 A/dm(2) for fluorine electrolysis. The enhanced electrochemical properties in electrode were due to proper pore distribution and size of pores, which effectively increased internal surface area.

결합제인 coal tar pitch와 petroleum cokes를 주원료로 결합제 첨가량을 변화시켜 불소 전해용 탄소 전극을 제조한 후 결합제 첨가가 전극특성에 미치는 영향을 조사하였다. 탄소전극의 특성은 물리적 특성, 기계적 강도, 그리고 KF·2HF 용액에서의 cyclic voltammogram과 0.5 M H2SO4 수용액에서 임피던스 스펙트로스코피의 전기화학적 거동을 통하여 평가하였다. 이 결과 결합제 45 wt%가 첨가된 경우 제일 양호한 전극특성을 나타냈으며 불소전해 시 임계전류밀도는 12.07 A/dm(2)로 가장 높은 값을 얻었다. 이와 같이 양호한 전극특성이 나타난 것은 전극표면에 존재하는 기공의 특성과 밀접한 관련이 있었으며 표면기공의 적절한 크기와 분포가 실질적으로 전극의 비표면적을 향상시켰기 때문이다.