In this study, blends of polystyrene(PS) and Styrene-Butadiene-Rubber(SBR) were prepared by mixing in the kneader, and then the foams of blends were prepared by extruding with a foaming agent in a single screw exturder. We investigated the physical properties and morphological behaviors of blended foams by UTM, SEM and Densitmeter. The number of cells in the foamed PS/SBR blends matrix increased as the processing temperature decreased. Also, the structure of cell changed from closed cell structure to open cell structure as SBR fraction increased. In PS/SBR blends, the impact strength was improved by adding SBR, however, the flexural strength was decreased except for the 5 wt% SBR.

본 논문에서는 polystyrene(PS) 발포체의 내충격성을 향상시키기 위해 polystyrene styrene butadiene rubber(PS/SBR)을 100:0, 95:5, 90:10, 80:20, 70:30 무게비율로 blending한후 일축압출기를 사용하여 발포체를 제조하였다. 압출발포 가공온도(170, 180, 190 ℃)와 SBR 함량에 따른 물성과 형태학적 변화를 UTM, SEM, 밀도계를 사용하여 측정하였다. 가공온도가 증가함에 따라 발포체의 밀도가 감소하였으며, 발포체의 cell의 개수가 증가하였다. PS/SBR블렌드인 경우 SBR 함량이 5 wt%를 제외하고는 PS 단독 발포체의 밀도와 비슷하거나 낮아졌으며, 내충격강도는 SBR 함량이 증가할수록 증가하였다. 또한 SBR 함량이 증가함에 따라 발포체 cell 구조가 closed cell에서 open cell로 변하는 경향을 보였으며 이에 따라 굴곡강도가 감소하는 경향을 보였다.