In order to improve the compatibility between polyporpylene (PP) and polyamide 66 (PA 66), different amounts (0,2,5, and 8 wt%) of polypropylene-grafted-acrylic and (PP-g-AA) compatibilizer were incorporated to prepare PP/PA 66 (85/15, 70/30, and 50/50) blends using reaction extrusion process. Then, thermal, mechanical and morphological characteristics of the compatibilized blends were investigated. In the dynamic mechanical analyses (DMA) of compatibilized PP/PA 66 (70/30) blends, the intensities and areas of the loss factor, tanδpeaks decreased. The βrelaxation temperatures (Tβ=Tg) of PA 66 slightly decreased proportional to the compatibilizer (PP-g-AA) while those of PP had no effect. In DSC measurements, the melting temperatures of both PP and PA 66 components slightly decreased proportional to the compatibilizer. The average size of PA 66 particles in the cryogenically fractured surface of PP-rich blends decreased with addition of the compatibilizer. The tensile strengths of the compatibilized blends had the maximum values with the increase of the compatibilizer content (2 wt% for 85/15 and 5 wt% for 70/30). The impact strengths of PP-rich blends (85/15 and 70/30) did not change with the compatibilizer, but it decreased with increasing compatibilizer content in PP/PA 66 (50/50) blends

잘 섞이지 않는 폴리프로필렌(PP)과 폴리아미드 66(PA 66)의 상용성을 개선하기 위하여 반응 압출 상용화제로 아크릴산 그라프트 PP를 여러 비율 (0,2.5 및 8 중량%)로 첨가하여 PP/PA 66 블렌드 (85/15, 70/30, 및 50/50)를 제조하였다. 블렌드의 상용화 정도를 알기 위해 열적 및 기계적 물성을 측정하였으며 파괴단면의 미세구조를 관찰하였다. PP/PA 66의 70/30(중량비) 블렌드에 대한 DMA 결과는 상용화제를 첨가함에 따라 손실 상수인 tanδ의 피크 높이 및 면적이 감소하는 결과를 보였으며 PA 66의 Tg는 약간씩 감소하였으나 PP의 Tg는 변화가 없었다. DSC 결과에서 두 고분자의 용융온도는 상용화제 첨가량에 비례하여 약간씩 감소하였다. 저온파쇄단면에서 분산 입자의 평균입자 크기는 상용화제 첨가에 따라 감소하였다. 상용화제를 첨가한 블렌드의 인장강도는 상용화제 첨가량에 따라 (85/15는 2 중량% 첨가시, 70/30은 5 중량% 첨가시) 최대값을 보였다. 충격강도는 PP가 많은 경우(85/15 및 70/30)상용화제 첨가시 거의 변화가 없었으나 50/50(PP/PA 66)에서는 상용화제 첨가에 의해 감소하는 경향을 보였다.