This study investigated the property of molybdenum precipitate formed with α-benzoinoxime by SEM, FTIR, TG-DTA, and XRD. The precipitate was produced by adding 2 wt%, α-benzoinoxime solution dissolved in 0.4 N NaOH to 1 M nitric acid solution containing 50 ppm molybdeum. The precipitate was composed of α-benzoinoxime-Mo precipitate and re-precipitate of α-benzoinoxime added excessively for increasing precipitation efficiency of molybdenum, α-benzoinoxime-Mo precipitate of these precipitates was dissolved in 0.4 N NaOH solution without hydrogen peroxide within 5 minutes, which proposed the possibility improving the existing process. As results of FTIR and TG-DTA, it was confirmed that α-benzoinoxime-Mo precipitate was formed by reaction of two α-benzoinoxime molecules and one MoO2+2. The form of α-benzoinoxime-Mo precipitate was amorphous

본 연구에서는 Mo을 α-benzoinoxime을 사용하여 침전반응시킬 때 생성되는 α-benoinoxime-Mo 침전물의 특성을 SEM, FTIR, TG/DTA와 XRD를 사용하여 조사하였다. 모의용액은 질산농도 1M, 50ppm Mo로 구성하였으며, 0.4 N NaOH에 용해된 2wc%의 α-benzoinoxime 용액을 첨가하여 침전물을 제조하였다. 생성된 침전물은 α-benzoinoxime-Mo 침전과 Mo의 침전율을 높여주기 위하여 과잉으로 첨가된 α-benzoinoxime의 재침전물로 구성되며 이 중 α-benzoinoxime-Mo 침전은 과산화수소를 첨가하지 않은 0.4 N NaOH용액으로 5분 내에 용해되어 기존 공정을 개선할 수 있었다. FTIR과 TG-DTA 결과로부터 Mo과 α-benzoinoxime은 두 분자의 α-benzoinoxime과 한 분자의 MoO2+2이온이 반응하여 α-benzoinoxime-Mo 침전물을 생성하였음을 확인할 수 있었으며, α-benzoinoxime-Mo 침전물은 무정형으로 나타났다.