EVA mixtures (EVAL) were obtained from ethylenevinylacetate resin emulsion(EVA) blended with acryl (ACR), epoxy (EPY) and styrenebutadiene rubber (SBR) latex (L) respectively in the range of 0~50wt% content. These EVALs were mixed with portland cement (CM) in the range of 0~60wt% and liquefied EVAL-CM composites were made and various of EVAL-CM composites as waterproof material were investigated. Viscosity was increased above 30wt% cement content. The workable time was 20~40min. The tact-free drying time was 60 min. Pencil hardness was 2H above 50wt % cement content. The value of water resistance was SBR>EPY>ACR latex and that of SBR added to EVAL-CM composites was most excellent. The bending adhesive and impact strength of SBR mixed to EVA-CM composites was most excellent in the range of 10~20 wt% latex content.

EVA 수지 에멀젼에 아크릴(ACR),에폭시(EPY) 및 스티렌부타디엔고무(SBR) 라텍스(L)를 각각 전체 혼합물 0~50wt%로 첨가하여 EVA 혼화제(EVAL)를 만들고 이것에 포틀랜드 시멘트(CM)를 전체 혼합물 중 0~60wt% 범위로 첨가하여 액상의 EVAL-CM 조성물을 얻었다. 이 EVAL-CM 조성물에 대하여 방수재로써의 여러 가지 특성을 실험하였다. 점도는 시멘트 함량 50wt% 잉상에서 상승하였다. 가사시간은 20~40분이었다. 지촉 건조 시간은 60분이었다. 연필 경도는 시멘트 함량 50wt% 이상에서 2H를 나타냈다. 내수성의 크기는 SBR>EPY>ACR 라텍스로써 SBR 라텍스를 첨가한 경우가 가장 우수하였다. 굴곡 강도, 접착 강도 및 충격 강도의 경우는 라텍스 함량 10~20wt%의 SBR를 첨가했을 때 가장 우수하였다.