The purpose of this paper is to investigate the durability of high performance cement composites using phenol resin manufactured by warm pressing. In order to improve the durability of MDF cement composite, the phenol resin, modifier and silane coupling agent were added to HAC/PVA based MDF cement composites. Dry flexural strength of high performance cement composite was decreased with increasing phenol resin content. However, the durability increased about 160% than those without phenol resin immersed 14 days in water. And, the durability is best condition in the all mixed with phenol resin, modifier and silane coupling agent. Specially, Flexural strength of 14 days immersion in water(durability) was retained about 60% of intial strength.

본 연구는 HAC/PVA 계 고성능 MDF 시멘트 복합재료의 내구성 향상을 위하여 레졸형 페놀수지, 개질제, 실란커플링제를 사용하여 저온가압 성형공정으로 제조된 고성능 MDF 시멘트 복합체의 내구성 특성은 다음과 같다. 페놀수지 함량이 증가될수록 건조 굽힘강도는 다소 감소하였으나, 내구성은 크게 향상되었다. 특히 페놀수지 함량 7% 첨가할 경우에 미첨가의 경우에 비하여 건조강도는 소폭감소 되었으나 14일 수분침적 강도는 160% 향상되었다. 또한 페놀수지와 개질제 및 실란 커플링제를 함께 첨가한 경우에 내구성이 가장 우수하였으며, 특히 14일 수분침적 굽힘강도(내구성)는 건조강도의 약 60% 수준을 유지하였다.