The specific capacitance characteristics of the electric double layer capacitors(ELDC) which were made of phenol based activated carbon fiber(ACF) electrodes. Also the effect of aqueous electrolytes on the cell performance has been investigated with respect to different specific surface areas of electrodes and different kinds of aqueous electrolytes. It has been shown that larger surface area and pore size, higher conductivity of electrodes, and higher ion mobility of electrolytes have better specific capacitances. It has been found that heat treatment at 1200℃ and CO2post-activation at 900℃ of the electrode are effective to improve the specific capacitance over 145F/g and 165F/g, respectively. The EDLC showed high efficiency and long cycle life over 30000 cycles.

고비표면적의 활성탄소섬유(ACF; activated carbon fiber)를 분극성 전극으로 이용한 전기이중층 캐패시터(electric double layer capacitor)의 단위 cell test를 통하여, ACF의 비표면적, 세공의 크기 및 전기전도도가 캐패시터의 비축전용량에 커다란 영향을 미치고 있음을 확인할 수 있었고, 전해질은 H+이온을 함유한 H2SO4이 가장 좋은 축전용량을 나타내었으나, 집전체 부식 등의 문제로 인하여, 실용화에 있어서는 우수한 충방전 거동을 나타낸 KOH계 전해질이 적당한 것으로 확인되었다. 분극성 전극으로 사용되는 ACF를 탄화 또는 후활성화 등이 후처리를 통하여 비축전용량을 급격히 증가시킬 수 있었고, 3만회까지의 연속 충방전 실험에서 전기이중층 캐패시터는 2차전지에서는 찾아볼 수 없는 매우 높은 충방전 효율과 긴 사용수명을 가지는 것을 확인할 수 있었다.