In this study, carbon fiber reinforced cement composites(CFRCs) reinforced with short noncircular type carbon fibers were fabricated and properties(drying shrinkage, resistance to freezing and thawing, and fracture toughness) were compared with those of the CFRCs reinforced with circular type carbon fibers. It was found that these properties greatly depended on the shape and length of carbon fibers. The drying shrinkage of CFRCs reinforced with C-type carbon fiber was superior to other CFRCs. This effect was increased with a high aspect ratio of fiber. The resistance to freezing and thawing was increased with the fiber length and fiber volume percent, but there was on remarkable effect to fiber shape. Fracture toughness and resistance to crack propagation of CFRCs reinforced with C-CFs were improved compared with other CFRCs. It was believed that the more absorption of fracture energy into the larger interface caused an increase in fracture toughness and resistance to crack propagation

본 연구에서는 비원형의 단-탄소섬유를 이용하여 시멘트 복합재를 제조하고 이 복합재의 특성(건조 수축, 동결 융해저항성, 파괴 인성)을 원형 탄소섬유보강 복합재와 비교하여 연구하였다. 그 결과 섬유의 형상과 길이에 크게 의존하였다. C형 탄소섬유보강 시멘트 복합재의 건조수축저감 효과가 다른 형상의 섬유보강 복합재에 비해 우수하였다. 이 효과는 섬유의 종횡비가 클수록 증가하였다. 또한, 동결융해 저항성은 섬유형상의 영향은 두드러지지 않았으나 섬유길이와 섬유함유율에 따라 증가하였다. 특히, C형 보강 시멘트 복합재의 파괴 인성 및 균열 저항성은 다른 것에 비해 크게 개선되었다. 이는 더 큰 계면으로 파괴에너지를 더 많이 흡수하였기 때문으로 생각된다.