Electrochemical properties of the Al current collector being used in lithium ion batteries have been studied in the 4 different aprotic electrolytes(1 M LiBF4EC : DMC, 1 M LiBF4EC : EMC. 1 M LiPF6EC : DMC. 1 M LiPF6EC : EMC) employing cyclic voltammetry and impedance measurement. Al electrode showed a wide range of the electrochemical window(0.5-4.1 V vs. Li/Li+). However, solid interfacial materials has been formed on the Al surface due to reduction of impurities(H2O, O2etc), lithium salts, and electrolytes at low applied potentials, and aluminum oxides in the highly oxidizing potential as well. Especially, Al current collector was susceptible to localized in consequence of impurities in electrolytes

리튬이온전지용 Al 집전체와 비수용성 전해질의 전기화학적 특성을 연구하기 위하여 1 M LiBF4EC : DMC, 1 M LiBF4EC : EMC. 1 M LiPF6EC : DMC. 1 M LiPF6EC : EMC의 4가지 전해질에서 전압전류 및 임피던스 특성을 조사하였다. Al 집전체는 비교적 넓은 전위창(0.5-4.1 V)에서 안전하지만, 첫 싸이클의 저 전위에서(<2.0 V vs. Li/Li+)에서 전해질 내 미량 존재하는 불순물(H2O), O2등)과 반응하여 계면물질을 생성하며, 리튬염 및 유기용매 또한 일정 전위 범위(<1.5 V vs. Li/Li+)에서 Al 집전체와 반응하였다. 특히 전해질내 존재하는 미량의 불순물로 인하여 고 전위에 노출된 Al 집전체의 국부부식이 진행되었다.