The production of fine metal oxide particles in supercritical water has been studied. Cobalt nitrate solution and manganese nitrate solution have been selected as model solutions for metal salt aqueous solution and the particles of cobalt oxide and manganese oxide have been produced. It was observed that the production of fine metal oxide particles in supercritical water was feasible and the dehydration rate was remarkably high in supercritical water. In spite of a short residence time (30∼100 seconds), fine particles (0.5∼2 μm) have been produced. In the supercritical water process, the temperature of mixer had a significant effect on particle size and size distribution. It was observed that a change in reaction temperature resulted in the control of particle size

초임계수를 이용한 금속산화물의 미세입자 제조에 대하여 연구하였다. 금속염 수용액으로는 cobalt nitrate solution과 manganese nitrate solution을 sample solution으로 선택하여 코발트산화물과 망간산화물 입자를 제조하였다. 얻어진 결과로부터 초임계수를 이용한 금속산화물 미세입자의 제조가 가능함을 확인할 수 있었으며, 초임계수 하에서는 매우 빠른 dehydration반응이 일어남을 관찰할 수 있었다. 짧은 반응시간(30∼100초)에도 불구하고 미세입자 (0.5∼2μm)가 생성되었으며, 초임계수 공정에서는 mixer의 온도가 입자의 크기 및 분포에 큰 영향을 미침을 알 수 있었다. 반응온도 조절을 통하여 입자의 크기를 제어할 수 있음을 확인할 수 있었다.