In this work, the adsorption characteristics of the activated carbon treated with 30 wt. %HCl and 30 wt. % NaOH were investigated. The acid and base values were determined by Boehm's method and the surface area and porosity was measured by BET-method with N2-adsorption. Also, the adsorption characteristics of the activated carbons treated with acid and base chemical solutions were investigated with CO2and NH3-adsorption. From which, relatively different adsorption behaviors of the modified activated carbons were observed in the amounts of CO2and NH3adsorptions, even though the physical surface structures of the activated carbons, such as specific surface area, pore size and pore volume, were not significantly changed.

본 연구에서는 활성탄소를 산성 및 염기성 용액으로 처리하여 pH변화에 따른 흡착 특성을 비교 분석하였다. 처리하지 않은 일반 활성 탄소와 30 wt. % HCl 및 30 wt. % NaOH 용액으로 처리된 활성탄소의 표면 산도 및 표면 염기도를 Boehm의 선택 중화법을 이용하여 측정하였으며, 그 흡착표면적과 기공도 등은 BET 법을 이용한 N2기체 흡착을 통해 알아보았다. 또한 산, 염기 처리된 활성탄소의 흡착 특성을 비교하기 위해 CO2및 NH3기체의 흡착 실험을 수행하였다. 그 결과 일반 활성탄소와 산성 또는 염기성 용액으로 각각 처리된 활성탄소의 물리적인 표면구조는 큰 변화를 나타내지 않았으나, CO2및 NH3에서의 흡착에 있어서 화학적 처리에 따른 서로 다른 표면 관능기에 의하여 상대적으로 향상된 흡착 거동을 나타내었다.