In this study, a water adsorbent was synthesized by radiation grafting of acrylic acid and multifunctional monomers such as 1,2-propanediol dimethacrylate (PDMA) and 1,1,1-trimethylolethane triacrylate (TMETA) onto cellulose and its subsequent treatment with 5% NaOH. Its absorbency on H2O and 0.9 % NaCl aqueous solution was examined. The highest absorbency on water and on 0.9% NaCl aqueous solution was obtained from the addition of 0.75vol% PDDMA and of 1.0vol% TMETA onto acrylic acid solution, respectively. The absorbency of commercial hygienic band on water and NaCl aqueous solution was 21g/g and 22g/g, respectively. However, that for acrylic acid-grafted cellulose including TMETA was 298g/g and 54g/g, respectively.

아크릴산과 가교제로서 1,2-propandiol dimethacrylate (PDDMA) 및 1,1,1-trimethylolethane triacrylate (TMETA)를 셀롤로오스에 방사선 그라프트 중합시킨 후 5% 수산화나트륨 수용액으로 처리하여 흡수성 재료를 제조한 다음, 순수한 물과 염화나트륨 수용액에 대한 흡수성에 대하여 고찰하였다. 가교제로서 다관능성 단량체가 포함된 아크릴산 그라프트 셀롤로오스의 흡수력은 PDDMA는 0.75부피%에서 TMETA는 1.0부피%에서 최대점을 나타내었다. 방사선 그라프트 중합법에 의하여 제조한 흡수성 셀룰로오스와 상용화된 여성용 생리용품과의 물 및 염화나트릅 수용액에 대한 흡수율을 비교해 본 결과 여성용 생리용품의 경우 물에 대한 흡수율은 21 g/g이고 염화나트륨 수용액에 대한 흡수율은 22 g/g을 나타내었으나, 본 방사선 그라프트 중합법에 의하여 제조한 셀롤로오스는 물과 염화나트륨 수용액에 대하여 최대 298 g/g, 54 g/g의 우수한 흡수능을 나타내었다.