This study provides the identification of corrosion cause substances in super heater tube from a commercial scale circulating fluidized bed boiler. Electricity is produced by the combustion of biomass mainly wood waste. The biomass, super heater tube, super heater tube ash, and boiler ash were collected and components associated with corrosion were analyzed. A large amount of oxygen-containing material was found due to oxidation. The chlorine content was analyzed as 6.1% and 4.3% in super heater tube ash and boiler ash respectively which were approximately 20 and 14 times higher than those of designed values. Also, alkaline metal contents (K, Na, Ca) were very high in ash samples collected from super heater tube and boiler. The tendency of slagging and fouling was predicted based on X-Ray Fluorescence (XRF) results. Basicity that can lead to slagging was estimated as 3.62 and 2.72 in super heater tube and boiler ash, respectively. Slagging would occur with ash content when considering the designed value as 0.35.

본 연구에서는 순환유동층 보일러 과열기 튜브의 부식 원인물질을 규명하여, 부식방지를 위한 방안을 모색하고자 하 였다. 연료, 과열기 튜브 부식부위, 과열기 튜브에 부착된 재 및 보일러 재를 채취하여 성분분석을 수행하였다. 과열기 튜브 부식부위에서 산화로 인한 O성분이 함유되어 있는 것을 확인하였다. 과열기 튜브 부착 재 및 보일러 재에서 6.1% 및 4.3%의 Cl이 분석되었으며, 이는 설계값의 약 14-20배 정도 높은 수치이다. 또한 알칼리 금속물질(K, Na, Ca) 의 함량이 매우 높게 분석되었다. XRF 데이터를 이용하여 보일러에서 재의 슬래깅과 파울링에 대한 영향을 예측하였 다. Basicity는 과열기 튜브 부착 재 및 보일러 재에서 각각 3.62 및 2.72로 산정되었으며, 설계값인 0.35에 비하여 높은 수치를 갖는 것으로 확인되었다.